304 VS 304L stainless steel
Dec 23, 2025
Leave a message
Related Specs and Trade names
304 VS 304L Stainless Steel
What sets 304 vs 304L apart? The key distinction lies in their carbon content. 304 stainless steel contains a maximum of 0.08% carbon, whereas 304L stainless steel has a lower carbon content, capped at 0.03%. This minimal reduction in carbon content has significant implications for the material's performance and applications.
The table below shows more clearly and visually the differences between the chemical composition of 304 vs 304L.
| ASTM | C % | Si % | Mn % | P % | S % | Ni % | Cr % | Mo % | N % | Cu % |
| 304 | 0.08 | 0.75 | 2 | 0.045 | 0.03 | 8.0 – 10.5 | 18.0–20.0 | – | 0.1 | – |
| 304L | 0.03 | 0.75 | 2 | 0.045 | 0.03 | 8.0-12.0 | 18.0-20.0 | – | 0.1 |
304 VS 304L Stainless Steel | Differences Caused
304 VS 304L | Physical Property
304 VS 304L stainless steel in physical properties are mainly as follows:
Density: Both are 7.93g/cm³.
Thermal Expansion: 304 17.2 μm/m-°C 304L 18.2 μm/m-°C.
304L has a slightly higher coefficient of thermal expansion than 304 which means that for the same temperature change, 304L will increase or decrease in length by a slightly higher percentage than 304.
Thermal Conductivity: 304 16.3 W/m-K 304L 14.6 W/m-K
304 has a slightly higher thermal conductivity than 304L, which means that 304 has a slightly better thermal conductivity than 304L.
304 VS 304L | Mechanical Property
304 VS 304L stainless steel in terms of mechanical properties are mainly reflected in the following aspects.
Tensile strength: At room temperature, the tensile strengths of 304 vs 304L are 515MPa and 485MPa, respectively, with 304 having a slightly higher tensile strength than 304L.
Yield strength: At room temperature, the yield strengths of 304 vs 304L are 205MPa and 170MPa, respectively, and 304 has a significantly higher yield strength than 304L.
Elongation: The elongation of 304 vs 304L are 45% and 35%, respectively, and 304 has a slightly higher elongation than 304L.
Impact toughness: Both 304 and 304L have higher impact toughness, but at low temperatures, 304L may have slightly higher impact toughness than 304.
304 VS 304L | Corrosion Resistance
304 VS 304L stainless steel in terms of corrosion resistance is mainly reflected in the following aspects.
Intergranular Corrosion: As we have mentioned before, 304L is more resistant to intergranular corrosion than 304 due to its low carbon content.
Acid Corrosion: In acidic media, low carbon gives 304L a more stable structure, making it less likely to react with acidic media and be corroded.
Chlorine Ions: Both 304 and 304L can not resistant to Chloride Ion corrosion
304 VS 304L | Heat Resistance
304 VS 304L stainless steel in terms of heat resistance is mainly reflected in the following aspects.
Carbon readily combines with Chromium to form carbides at high temperatures. 304L steel contains a low carbon content, and only a very small amount of carbon can react with chromium, the remaining Chromium can continue to protect the stainless steel on the surface. As a result, 304L is relatively stable in high-temperature environments and is much less prone to deformation or stress cracking.
In addition, 304L stainless steel has better oxidation resistance and can maintain its material properties at higher temperatures. For this reason, 304L is often preferred in high-temperature applications.
304 VS 304L | Weldability
304 VS 304L stainless steel in terms of weldability is mainly reflected in the following aspects.
During the welding process, 304L is less prone to intergranular corrosion due to its low carbon content, which means that the grains around the weld are less prone to precipitation, thus ensuring the corrosion resistance of the welded joint.
Since the coefficient of thermal expansion of 304L is smaller than 304, 304L is more prone to defects such as warpage and cracking compared to 304 during welding due to thermal stress. To avoid this, proper welding techniques and measures are needed, such as controlling welding temperature, preheating, etc.
We provide a comprehensive range of stainless steel grades, including the widely used 304 and 316 series, as well as specialized grades such as 430, 201, duplex, and super austenitic steels, tailored to meet diverse industrial and environmental requirements. Whether you need corrosion-resistant solutions for marine applications, food-grade compliance, high-temperature durability, or custom specifications, our expert team is ready to assist.
Our factory
As a professional stainless steel product manufacturer, we possess a complete modern production line encompassing precision slitting, laser cutting, CNC bending, automatic welding, and sophisticated surface treatment. Leveraging advanced processing equipment and a rigorous quality control system, we specialize in producing high-quality stainless steel products that meet international standards, including industrial components, building materials, household goods, and special customized parts.
Stainless steel packaging
To ensure that our stainless steel products are protected from scratches, impacts, and corrosion during transportation and storage, we provide professional packaging solutions: precision surfaces are protected with electrostatic protective film or peelable anti-corrosion coatings; pipes and plates are secured with waterproof wrapping film and custom-made corner protectors; standard parts are packaged in anti-rust bags and blister trays; and outer cartons are clearly marked with moisture-proof and "this side up" labels. All packaging adheres to export standards, balancing protection, environmental friendliness, and ease of unpacking, guaranteeing that products arrive in perfect condition to our global customers.
Send Inquiry