Premium AISI 316Ti Titanium-Stabilized Stainless Steel in China

🧪 Chemical Composition

Element	Composition (%)
Carbon (C)	≤ 0.08
Manganese (Mn)	≤ 2.00
Silicon (Si)	≤ 0.75
Phosphorus (P)	≤ 0.045
Sulfur (S)	≤ 0.030
Chromium (Cr)	17.0 - 20.0
Nickel (Ni)	10.0 - 14.0
Molybdenum (Mo)	2.0 - 3.0
Titanium (Ti)	5×C min - 0.70 max
Nitrogen (N)	≤ 0.10
Iron (Fe)	Balance

⚙️ Mechanical Properties

Property	Value
Tensile Strength (Rm)	515 - 690 MPa
Yield Strength (Rp0.2)	≥ 205 MPa
Elongation (A5)	≥ 40%
Reduction of Area (Z)	≥ 60%
Hardness (HB)	≤ 217
Hardness (HRC)	≤ 22
Impact Energy (KV) at 20°C	≥ 60 J
Fatigue Limit (107 cycles)	240 MPa
Young's Modulus (E)	200 GPa
Shear Modulus (G)	81 GPa
Poisson's Ratio (ν)	0.27 - 0.30

🔬 Physical Properties

Property	Value
Density	8.0 g/cm³
Melting Point	1400 - 1450°C
Thermal Conductivity at 20°C	16.3 W/m·K
Thermal Conductivity at 100°C	17.8 W/m·K
Thermal Expansion (20-100°C)	16.0×10-6/K
Thermal Expansion (20-300°C)	16.8×10-6/K
Specific Heat Capacity	500 J/kg·K
Electrical Resistivity at 20°C	0.74 µΩ·m
Magnetic Permeability	1.02 µr (max)
Curie Temperature	Non-magnetic

📏 Product Specifications

Specification	Available Options
Product Forms	Bars, Rods, Plates, Sheets, Strips, Tubes, Pipes, Forgings, Castings
Bar Diameter Range	6 mm - 300 mm
Plate Thickness Range	3 mm - 150 mm
Sheet Thickness Range	0.4 mm - 6 mm
Tube OD Range	6 mm - 219 mm
International Standards	ASTM A240, A276, A312, A479, EN 1.4571, JIS SUS316Ti, GB/T 1220
Surface Finishes	Hot Rolled, Cold Rolled, 2B, BA, No.4, HL, Mirror, Pickled
Dimensional Tolerances	ASTM, EN, JIS standard tolerances or custom requirements
Length Options	Standard lengths or cut-to-length as specified
Edge Conditions	Mill Edge, Slit Edge, Sheared Edge, Deburred