Stainless Steel Grade 309S - High Temp Alloy Steel Grade
Feb 05, 2026
Leave a message
Chemical Composition
The following table shows the chemical composition of grade 309S stainless steel.
| Element | Content (%) |
|---|---|
| Iron, Fe | 60 |
| Chromium, Cr | 23 |
| Nickel, Ni | 14 |
| Manganese, Mn | 2 |
| Silicon, Si | 1 |
| Carbon, C | 0.080 |
| Phosphorous, P | 0.045 |
| Sulfur, S | 0.030 |
Physical Properties
The physical properties of grade 309S stainless steel are given in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8 g/cm3 | 0.289 lb/in³ |
| Melting point | 1454°C | 2650°F |
Mechanical Properties
The mechanical properties of annealed grade 309S stainless steel are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength, ultimate | 620 MPa | 89900 psi |
| Tensile strength, yield (0.2%) | 310 MPa | 45000 psi |
| Izod impact | 120 - 165 J | 88.5 - 122 ft-lb |
| Modulus of elasticity | 200 GPa | 29000 ksi |
| Shear modulus | 77 GPa | 11200 ksi |
| Poissons ratio | 0.3 | 0.3 |
| Elongation at break (in 50 mm) | 45% | 45% |
| Hardness, Brinell (converted from Rockwell B hardness) | 147 | 147 |
| Hardness, Knoop (converted from Rockwell B hardness) | 164 | 164 |
| Hardness, Rockwell B | 85 | 85 |
| Hardness, Vickers (converted from Rockwell B hardness) | 169 | 169 |