Stainless Steel Grade 316 - Industrial Corrosion Resistant

 

Composition

Table 1. Composition ranges for 316 grade of stainless steels.

Grade		C	Mn	Si	P	S	Cr	Mo	Ni	N
316	Min	-	-	-	0	-	16.0	2.00	10.0	-
	Max	0.08	2.0	0.75	0.045	0.03	18.0	3.00	14.0	0.10
316L	Min	-	-	-	-	-	16.0	2.00	10.0	-
	Max	0.03	2.0	0.75	0.045	0.03	18.0	3.00	14.0	0.10
316H	Min	0.04	0.04	0	-	-	16.0	2.00	10.0	-
	max	0.10	0.10	0.75	0.045	0.03	18.0	3.00	14.0	-

 

Mechanical Properties

Table 2. Mechanical properties of 316 grade stainless steels.

Grade	Tensile Str (MPa) min	Yield Str 0.2% Proof (MPa) min	Elong (% in 50 mm) min	Hardness
				Rockwell B (HR B) max	Brinell (HB) max
316	515	205	40	95	217
316L	485	170	40	95	217
316H	515	205	40	95	217

 

Note: 316H also has a requirement for a grain size of ASTM no. 7 or coarser.

Physical Properties

Table 3. Typical physical properties for 316 grade stainless steels.

Grade	Density(kg/m3)	Elastic Modulus (GPa)	Mean Co-eff of Thermal Expansion (µm/m/°C)			Thermal Conductivity (W/m.K)		Specific Heat 0-100 °C (J/kg.K)	Elec Resistivity (nΩ.m)
			0-100 °C	0-315 °C	0-538 °C	At 100 °C	At 500 °C
316/L/H	8000	193	15.9	16.2	17.5	16.3	21.5	500	740

 

Grade Specification Comparison

Table 4. Grade specifications for 316 grade stainless steels.

Grade	UNS No	Old British		Euronorm		Swedish SS	Japanese JIS
		BS	En	No	Name
316	S31600	316S31	58H, 58J	1.4401	X5CrNiMo17-12-2	2347	SUS 316
316L	S31603	316S11	-	1.4404	X2CrNiMo17-12-2	2348	SUS 316L
316H	S31609	316S51	-	-	-	-	-