SUS409L Stainless Steel: Automotive Exhaust System Material

Chemical Composition of ASTM A268 409 S40900 Grade and EN 10088-2 1.4512 1.4516 Stainless Steel

Grade	–	C	Mn	Si	P	S	Cr	Ni	Ti
A268 409	min. max.	– 0.08	– 1.00	– 1.00	– 0.045	– 0.030	10.5 11.7	– 0.50	6×C-0.75
TP409L	min. max.	– 0.035	– 1.00	– 1.00	– 0.045	– 0.030	10.5 11.7	– 0.50	6×C-0.75
1.4516	min. max.	– 0.08	– 1.50	– 0.70	– 0.040	– 0.015	10.5 12.5	0.50-1.50	0.05-0.35
1.4512	min. max.	– 0.030	– 1.00	– 1.00	– 0.040	– 0.015	10.5 12.5	– 0.50	6×(C+N)-0.65

 

 

Mechanical properties of ASTM A268 409 Grade and EN 10088-2 1.4512 stainless steel

Grade	Tensile Strength	Yield Strength 0.2% Proof	Elongation	Hardness	Hardness
Grade	ksi(MPa) min	ksi (MPa) min	(% in 50mm) min	Rockwell B (HR B) max	Brinell (HB) max
409	55 (380)	25 (170)	20	95	207
1.4512	380-560	210	25

 

Testing and Documentation: Factory test certificate, EN 10204 3.1, chemical report, mechanical report, destructive testing report, non-destructive testing report, PMI test report, visual inspection report, third-party inspection report, NABL certified laboratory report.
Packaging: Wooden crate packaging, bubble wrap packaging, steel strapping, or packaging according to customer requirements.