409 Stainless Steel Plate
Grade 409 is a stabilized ferritic general purpose stainless steel with 11% chromium. It is especially useful for applications requiring oxidation or corrosion protection beyond the capability of carbon steel and some coated steels. 409 has good oxidation resistance and formability, but lower corrosion resistance due to the chromium content. 409 is not as corrosion resistant as 304, 430 or 439 grades, however, 409 is far superior to mild carbon steel. 409 can be formed by roll forming, stretch bending, deep drawing or pressing. In the annealed condition 409 does not harden when cold worked using mild roll forming techniques including pressing or stretch-bending. Welding performance for grade 409 is fair. This stainless steel material should not be used in impact-loaded structures, because in heat affected zones the grain structure can grow which may have a direct effect on the mechanical properties. 409 is commonly used for tubing and stampings in motor vehicle exhaust system applications.
Chemical Compositions*
| Element | % Present (in product form) |
|---|---|
| Carbon (C) | 0.030 |
| Silicon (Si) | 1.00 |
| Manganese (Mn) | 1.00 |
| Phosphorous (P) | 0.040 |
| Sulfur (S) | 0.015 |
| Chromium (Cr) | 10.50 - 12.50 |
| Molybdenum (Mo) | 6 x (C+N) to 0.65 |
| Iron (Fe) | Balance |
1. What is the equivalent grade of 409 stainless steel plate and its key chemical composition?
Equivalent grades: 1.4512 (EN), X2CrTi12 (DIN). Key composition: 10.5-12.5% Cr, ≤0.08% C, 0.15-0.50% Ti, ≤1.0% Mn. Ti ensures good weldability and corrosion resistance.
2. What are the main application fields of 409 stainless steel plates?
Widely used in: Automotive exhaust systems, heat exchangers, furnace parts, decorative trim, and low-corrosion industrial equipment.
3. What are the common international standards for 409 stainless steel plates?
Main standards: EN 10088-2 (Europe), ASTM A240/A480 (North America), JIS G 4305 (Japan), GB/T 3280 (China, equivalent to 022Cr11Ti).
4. What are the typical mechanical properties of 409 stainless steel plates (annealed state)?
Tensile strength ≥415 MPa, yield strength ≥205 MPa, elongation ≥20%. Good high-temperature resistance and formability.
5. What advantages does 409 stainless steel plate have compared to austenitic stainless steels (e.g., 304)?
Lower cost, better high-temperature oxidation resistance, and lighter weight. Suitable for low-corrosion, cost-sensitive applications.
Hot Tags: 409 stainless steel plate, China 409 stainless steel plate manufacturers, suppliers, factory, Stainless Steel Bright Annealed Plate, 310S Stainless Steel Sheet, 316 Stainless Steel Sheets, Stainless Steel Brushed Plate, Stainless Steel Mirror Plate, 904L Stainless Steel Plate