AISI 2507 Super Duplex Stainless Steel for customer
Mar 23, 2026
Leave a message
🧪 Chemical Composition
| Element | Composition (%) |
|---|---|
| Carbon (C) | ≤ 0.030 |
| Manganese (Mn) | ≤ 1.20 |
| Silicon (Si) | ≤ 0.80 |
| Phosphorus (P) | ≤ 0.035 |
| Sulfur (S) | ≤ 0.020 |
| Chromium (Cr) | 24.0 - 26.0 |
| Nickel (Ni) | 6.0 - 8.0 |
| Molybdenum (Mo) | 3.0 - 5.0 |
| Nitrogen (N) | 0.24 - 0.32 |
| Copper (Cu) | ≤ 0.50 |
| Tungsten (W) | ≤ 0.50 |
| Iron (Fe) | Balance |
⚙️ Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength (Rm) | ≥ 800 MPa |
| 0.2% Proof Strength (Rp0.2) | ≥ 550 MPa |
| Elongation (A5) | ≥ 15% |
| Hardness (HRC) | ≤ 32 |
| Impact Energy (KV) at 20°C | ≥ 60 J |
| Impact Energy (KV) at -40°C | ≥ 40 J |
| Fatigue Limit (10^7 cycles) | 350 MPa |
| Young's Modulus | 200 GPa |
| Shear Modulus | 80 GPa |
| Poisson's Ratio | 0.27 |
🔬 Physical Properties
| Property | Value |
|---|---|
| Density | 7.80 g/cm³ |
| Melting Point | 1350-1400°C |
| Thermal Conductivity at 20°C | 14 W/m·K |
| Thermal Conductivity at 100°C | 16 W/m·K |
| Thermal Expansion (20-100°C) | 13.0×10-6/K |
| Thermal Expansion (20-300°C) | 13.5×10-6/K |
| Specific Heat Capacity | 480 J/kg·K |
| Electrical Resistivity at 20°C | 0.85 µΩ·m |
| Magnetic Permeability | 1.02 µr |
| Curie Temperature | Non-magnetic |